A-PRESIDENT ZENIT Nano - Ceramic Composite Kit

Print
Description

Nano Composite is a composite that can be cured with light and polished with high brightness. It includes ultra-thin radio-opaque porcelain filling that is used for the treatment of adhesive filling. It can be polished with high brightness.
Thanks to its ultra-thin particle filling there can be made homegenous restorations. Chameleon effect enable tehe composite to perfectly adapt to the structure of the teeth. It is compatible with DIN EN ISO 24 049 Zenit Nano Ceramic Composite is presented in easy to use syringe.

Technical Specifications

 Vickers Hardness 1088 Mpa
 E-Module 18154 Mpa
 Compressive Strength 462 Mpa
 Flexural Strength 152 Mpa
 Tensile Strength 66 Mpa
 Shrinkage Rate 1,83%
 Radiopacity 220% Al

Indications
• Direct anterior and posterior restorations in black’s class I, II, III, IV and V cavities
• Indirect restorations such as inlays, onlays and laminate veneers
• Extended fissure sealing in molars and premolars
• Cores
• Splinting mobile teeth
• Adjusting the contours and shade to improve aesthetics

Zenit Nano Composite
• Light-curing Nano-Composite with outstanding physical properties and optimized handling
• New advanced formula
• Reduced shrinkage
• For all cavity classes
• Particle size 15–20nm (11% of content – weight)
• Very high filler content of 83% the expanded particle surface and the higher density can bear a higher load

Benefit From
• Excellent handling properties
• Ultrafine filler
• Extremely homogeneous restorations
• Excellent polishability
• Shade of the filling matches the tooth structure

Abrasion Resistance
• Loss of only 60 microns of Nano Composite material after 200,000 mastication cycles in a mastication simulator
• Result: more occlusal force in vitro than in conventional hybrid composites

Less Shrinkage
• Less polymerization shrinkage
• 1,83% average total
• Reduces danger of gaps

Photo courtesy of: Prof. Kunzelmann, University of Munich
• Nano Composite reduces the tensions in the filling
• Thanks to nano-agglomerates, the polymerization shrinkage is decreased
• Therefore, there is less stress in the filling

Resim1

Scratch resistant filling surface
• Very good polishing behavior
• Nano Composite feels smooth on the tongue
• Low absorption of water
• Color-stable
• No discoloration

Packaging Details
• 7x4gr Syringe (A1, A2, A3, A3.5, B2, A2O, W2)
• 1X5ml Prebond (5th Generation Adhesive System)
• 1x3ml Etching Gel
• Dynamic Flow Refill A2 shade
• 1x1 pcs shade guide
• 1x50 pcs applicator
• 1x4 pcs mixing well
• User guides